Saddle Spall Failure Investigation – by Touchstone Research Laboratory
A company with a Ni-hard cast iron roll had a large saddle spall failure, and Touchstone failure analysis experts were called in to determine the cause.
Evaluation of the fracture found that one side of the spall had been heated more than the other. This was indicated by the depth of firecracks.
This knowledge and observation prompted a review of rolling records. It was learned that a mill wreck had occurred just prior to the roll failure and that no examination of the mill rolls had been performed.
That led to the determination that the cause of the failure was overheating from long contact with the strip after the mill wreck.
If you need failure analysis in this or other areas, don’t hesitate to contact us.
Our other areas of expertise include:
The foundry is now a preferred supplier for many domestic users of wear-resistant cast iron parts.
Touchstone followed-up its detections with specific suggestions to eliminate the problem.
- Failure Analysis Index
- Corrosion Evaluation
- Light Microscopy
- Mechanical Testing
- Metallography
- Research & Development
- Scanning Electron Microscopy
For a PROMPT response, e-mail info@trl.com, call 304-547-5800, or visit us – we are conveniently located less than an hour from Pittsburgh International Airport and two hours from Columbus, Ohio.
Come visit us:
Come and get to know us. We value building long term relationships. The better we understand you and the issues you face, the better service we can offer.
Contact us today to discuss your failure analysis needs.
Failure Analysis Examples
If you don’t see a case study related to your interests, please contact us, as we likely have solved the same or similar problem in the past.